| LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Antistatic property,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2160 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 56.2 | MPa | ASTM D638 |
| fracture | 49.6 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 100 | % | ASTM D638 |
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 2160 | MPa | ASTM D790 |
| bending strength | 84.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 640 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 38.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 99.4 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 199 to 210 | °C | |
| Barrel middle temperature | 210 to 221 | °C | |
| Barrel front temperature | 221 to 232 | °C | |
| Processing (melt) temperature | 199 to 232 | °C | |
| Mold temperature | 38 to 54 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |