| Supplier | DSM |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Good stripping performance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Apparent density | 0.76 | g/cm³ | ISO 60 |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt volume flow velocity | 4 | cm³/10min | ISO 1133 |
| temperature | 230 | °C | ISO 1133 |
| load | 2.16 | kg | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 212 | ℃ | ISO 11357-1/-3 |
| Vicat Softening Temp | |||
| B50 | 125 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 1.85E-4 | /℃ | ISO 11359-1/-2 |
| Combustibility (1.5mm thickness) | HB | class | IEC 60695-11-10 |
| Test thickness | 1.6 | mm | IEC 60695-11-10 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1 MHz | 3.4 | IEC 60250 | |
| Dissipation factor | |||
| 100 Hz | 110 | E-4 | IEC 60250 |
| Volume resistivity | 1E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 0.6 | % | ISO 62 |
| Moisture absorption rate | 0.2 | % | Sim. to ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | N | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 280 | MPa | ISO 527-1-2 |
| Yield stress | 22 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | >50 | % | ISO 527-1/2 |
| Stress at 5% strain | 12.5 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 18 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 21 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 22 | MPa | ISO 527-1/-2 |
| Stress at 300% strain | 20 | MPa | ISO 527-1/-2 |
| Fracture stress | 31.5 | MPa | ISO 527-1/-2 |
| Fracture strain | >300 | % | ISO 527-1/-2 |
| tear strength | 176 | kN/m | ISO 34-1 |
| Shore hardness D (3s) | 60 | – | ISO 868 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |