| TAROLOY 50 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include: Flame Rated Impact Resistant Chemical Resistant Good Dimensional Stability&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good Dimensional Stability,Solvent resistance,low-temperature impact resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 30 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 0.80 to 1.1 | % | Internal Method |
| MD | 0.80 to 1.1 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.10 | % | ISO 62 |
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 90.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | 90.0 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| A50 | 170 | ℃ | ISO 306/A50 |
| Ball pressure test | |||
| 135℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 9.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3 mm | 18 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 110 | °C | |
| Pre-drying equipment | 110 to 120 | °C | |
| Drying time | |||
| — | 2.0 | hr | |
| Pre-drying equipment | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 20000 hrs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |