| 埃奇得 2018HA是一种茂金属催化乙烯-乙烷共聚物。 由埃奇得 2018HA具有卓越的抗张强度、冲击强度和抗穿刺性。 这些卓越的强度性能连同良好的拉伸性能使其成为通用的包装膜树脂。 其较高的熔融指数同样使该聚合体可理想地混合到富含低密度聚乙烯的薄膜中。&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | mPE |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, MD | 164 | MPa | ASTM D882 |
| 1% secant, TD | 182 | MPa | ASTM D882 |
| tensile strength | |||
| MD, yield | 9.09 | MPa | ASTM D882 |
| TD, yield | 9.07 | MPa | ASTM D882 |
| MD, fracture | 60.2 | MPa | ASTM D882 |
| TD, fracture | 56.1 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture | 590 | % | ASTM D882 |
| TD, fracture | 700 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 18 | ASTM D2457 | |
| Haze | 37 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |