| About |
|---|
| Gramid N200GL is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific or Europe. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Grand |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | V-2 |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.4 | % | ISO 294-4 |
| MD | 1.4 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 15512 |
| Relative viscosity | 2.7 | ISO 307 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 200 | ℃ | ISO 75-2/B |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | |||
| 2 mm | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 32 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| 3.00 mm | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | -3.3 | YI | ASTM D1925 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3100 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 86.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 25 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2700 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 100 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |