Boltaron 4332 - SOLIAO

About
Impact resistance of 20 ft lbs/in (1060 J/m) and other outstanding properties make Boltaron 4332 the ultimate Acrylic/PVC alloy for your most demanding applications Boltaron 4332 sheet is a proprietary, fire retardant, PVC/Acrylic alloy that offers outstanding physical properties, making it the ideal material from which to thermoform and fabricate parts subjected to high impact, abrasion, harsh chemicals and/or temperature extremes. With an Izod impact rating of 20 ft lbs/in (1060 J/m) Boltaron 4332 is among the most impact resistant PVC/Acrylic alloys ever produced. It is also exhibits extreme resistance to heat deformation and cold weather cracking, and is highly resistant to caustic and acidic chemicals spanning the entire pH range, in addition to offering greater abrasion resistance than stainless steel. At the same time, Boltaron 4332 is non-hygroscopic, eliminating the time and cost associated with pre-drying other thermoplastics, and is readily thermoformed, yielding uniform wall thickness in deep recesses and on sharp outside corners. It is also readily sawn, drilled, tapped, routed and otherwise machined using conventional tools, and can be brake formed (thinner gauges), heat welded, adhesive bonded and mechanically fastened, allowing rapid fabrication of a broad range of high-integrity parts and assemblies. Easy to use but difficult to damage, Boltaron 4332 eliminates the compromise associated with lesser PVC/acrylic alloys, FR ABS, and other fire rated thermoplastics, meeting and exceeding the most demanding requirements of fomers, fabricators and OEMs alike.&&

About

Impact resistance of 20 ft lbs/in (1060 J/m) and other outstanding properties make Boltaron 4332 the ultimate Acrylic/PVC alloy for your most demanding applications Boltaron 4332 sheet is a proprietary, fire retardant, PVC/Acrylic alloy that offers outstanding physical properties, making it the ideal material from which to thermoform and fabricate parts subjected to high impact, abrasion, harsh chemicals and/or temperature extremes. With an Izod impact rating of 20 ft lbs/in (1060 J/m) Boltaron 4332 is among the most impact resistant PVC/Acrylic alloys ever produced. It is also exhibits extreme resistance to heat deformation and cold weather cracking, and is highly resistant to caustic and acidic chemicals spanning the entire pH range, in addition to offering greater abrasion resistance than stainless steel. At the same time, Boltaron 4332 is non-hygroscopic, eliminating the time and cost associated with pre-drying other thermoplastics, and is readily thermoformed, yielding uniform wall thickness in deep recesses and on sharp outside corners. It is also readily sawn, drilled, tapped, routed and otherwise machined using conventional tools, and can be brake formed (thinner gauges), heat welded, adhesive bonded and mechanically fastened, allowing rapid fabrication of a broad range of high-integrity parts and assemblies. Easy to use but difficult to damage, Boltaron 4332 eliminates the compromise associated with lesser PVC/acrylic alloys, FR ABS, and other fire rated thermoplastics, meeting and exceeding the most demanding requirements of fomers, fabricators and OEMs alike.&&

Product Description
Generic	PMMA+PVC
Material Status	Commercial: Active
Features	High impact resistance,Flame Characteristics,Good tear strength,Good wear resistance,Solvent resistance
Availabilitys	North America
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	1100	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed	75.3	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
1.00 mm	V-0 5VB		UL 94
3.20 mm	V-0 5VA		UL 94
FAA Flammability			FAR 25.853
1.02 mm	12.0	sec	FAR 25.853
3.18 mm	60.0	sec	FAR 25.853

Supplementary information	Nominal value	Unit	Test method
Forming temperature	168 to 196	℃

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	106		ASTM D785
tensile strength
yield	39.3	MPa	ASTM D638
Bending modulus	2120	MPa	ASTM D790
bending strength
yield	60.0	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
2. Pass
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.