| Clariant Nylon 6 PA-211CF30 TF15是一种聚酰胺6（尼龙6）材料,含有的填充物为30% 碳纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 Clariant Nylon 6 PA-211CF30 TF15的主要特性有: 阻燃/额定火焰 Flame Retardant 传导性 高强度 加工性能良好 典型应用领域包括: 电线电缆 军事应用 商业/办公用品 体育用品 医疗/保健&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good Dimensional Stability,Conductive,Low coefficient of friction,Corrosion Resistant,Flame Characteristics,Lubricating,Good wear resistance,Solvent resistance,Good coloring,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.25 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 213 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 216 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 1.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 210 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 14500 | MPa | ASTM D790 |
| bending strength | 290 | MPa | ASTM D790 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 88 | ASTM D785 | |
| R-level | 123 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 249 to 274 | °C | |
| Barrel middle temperature | 249 to 274 | °C | |
| Barrel front temperature | 249 to 274 | °C | |
| Processing (melt) temperature | 254 to 271 | °C | |
| Melt temperature (target) | 266 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |