| Non-halogenated flame retardant Flexible NORYL extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced tensile elongation, capable of VW-1 performance and 105C temperature rating as defined by UL 1581. 87 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0mm wire with 0.12mm X 20 stranded coppoer conductor.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 16 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 30 seconds | 87 | ASTM D2240 | |
| tensile strength | |||
| fracture | 16.0 | MPa | ISO 527-2/50 |
| fracture | 27.0 | MPa | UL 1581 |
| fracture | 16.0 | MPa | ASTM D638 |
| Fracture, 136 ℃ | 26.0 | MPa | UL 1581 |
| Tensile strain | |||
| fracture | 170 | % | ISO 527-2/50 |
| fracture | 250 | % | UL 1581 |
| fracture | 180 | % | ASTM D638 |
| Fracture, 136 ℃ | 190 | % | UL 1581 |
| Bending modulus | 45.0 | MPa | ISO 178 |
| 100 mm span | 48.0 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -40.0 | ℃ | ASTM D746 |
| UL temperature rating | 105 | ℃ | UL 1581 |
| Heat Deformation（121℃） | 10 | % | UL 1581 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.2 to 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 2 mm in oil | 23 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 3.5E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 29 | % | ISO 4589-2 |
| Smoke density | ASTM E662 | ||
| Flame，0.5 mm plaque，Ds，max | 150 | ASTM E662 | |
| Non-Flame，0.5 mm plaque，Ds，max | 110 | ASTM E662 | |
| VW-1 | Pass | UL 1581 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 180 to 220 | °C | |
| Barrel 3 zone temperature | 220 to 250 | °C | |
| Barrel 5 zone temperature | 220 to 250 | °C | |
| Melt temperature | 220 to 250 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 3. Type I, 2.0 in/min |
| 4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 6. 0.49 in/min |
| 7. 2.0mm wire with 0.12 mm x 20 stranded copper |
| 8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 9. Plaque |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |