| Taitalac ABS 1002 is a high flow resin that features outstanding processability and high productivity. Uses include large or complex shaped products, TV housings, vacuum cleaners, various leisure goods, air conditioners, cash registers and floppy disks.&& |
| Product Description | |
|---|---|
| Supplier | Taita |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity,Quick molding cycle,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.3 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，12.7mm | 230 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 82.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 97.8 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance, 1.60 mm | 60.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.60 mm | 60.0 | ℃ | UL 746 |
| 1.60 mm | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| High Arc Burning Index (HAI) (1.57 mm) | 200 | UL 746 | |
| High voltage arc marking rate (HVTR) (1.57 mm) | 0.00254 | mm/min | UL 746 |
| Hot wire ignition (HWI) (1.57 mm) | 16 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 112 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃, 3.18 mm | 40.7 | MPa | ASTM D638 |
| Fracture, 23 ℃, 3.18 mm | 35.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 30 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2550 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃ | 71.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.11 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |