| Additive free C6 m-LLDPE for extrusion coating, injection moulding and compounding. Benefits & Features outstanding ESCR performance improved sealing performance improved mechanical properties Applications For extrusion coating: extrusion coating polymer for high demand on sealing and mechanical performance For injection moulding and compounding: absence of any kind of additive allowing tailor formulation of specific compounds and master-batches&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Low density,High ESCR |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.914 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 15 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Compression Molding | 175 | hr | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -20 ℃, molded | 71 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 90.0 | ℃ | ISO 306/A50 |
| Melting temperature | 96.0 to 114 | ℃ | ISO 11357-3 |
| Crystallization peak temperature | 84 to 100 | ℃ | Internal Method |
| Fusion heat | 104 | J/g | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 46 | ISO 868 | |
| Tensile modulus | |||
| Compression Molding | 217 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃, molded | 9.00 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Yield, molding | 22 | % | ISO 527-2 |
| Fracture, molded | > 600 | % | ISO 527-2 |
| Bending modulus | |||
| 23 ℃, molded | 244 | MPa | ISO 178 |
| Tensile fracture strength | |||
| Compression Molding | No Break | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | < 280 | °C | |
| Melt temperature | < 280 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. DSC 2nd heating 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |