| About |
|---|
| Rilsamid® AZM 30 O TLD resin is a fiberglass reinforced polyamide. This natural grade is designed for injection moulding. This grade is also available in green (Rilsamid® AZM 30 Green 56827 TLD resin) and grey (Rilsamid® AZM 30 Grey 632 TLD resin).&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 235℃，5 kg | 14.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 80 | ISO 868 | |
| Shore D, 15 seconds | 77 | ISO 868 | |
| Tensile modulus | 6450 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 116 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 6.0 | % | ISO 527-2 |
| Bending modulus | 5300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 19 | kJ/m² | ISO 179 |
| 23℃ | 28 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 98 | kJ/m² | ISO 179 |
| 23℃ | 90 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 180 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA12, MHLR, 14-070, GF 30 | ISO 1874 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 40 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |