LUVOCOM® 3F PEEK CF 9710 BK

About
LUVOCOM® 3F PEEK CF 9710 BK is a Polyetheretherketone (PEEK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for 3d printing, fused filament fabrication (fff) or extrusion. Important attributes of LUVOCOM® 3F PEEK CF 9710 BK are: Flame Rated Chemical Resistant Flame Retardant High Stiffness High Strength Typical applications include: Aerospace Electrical/Electronic Applications&&

About

LUVOCOM® 3F PEEK CF 9710 BK is a Polyetheretherketone (PEEK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for 3d printing, fused filament fabrication (fff) or extrusion. Important attributes of LUVOCOM® 3F PEEK CF 9710 BK are: Flame Rated Chemical Resistant Flame Retardant High Stiffness High Strength Typical applications include: Aerospace Electrical/Electronic Applications&&

Product Description
Supplier	Lehmann
Generic	PEEK
Material Status	Commercial: Active
Features	Good Rigidity,Flame Characteristics,Solvent resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	ISO 1183
Melt Volume Rate
380℃，10 kg	10.0	cm³/10min	ISO 1133
Shrinkage rate
3.0 mm	0.20 to 0.40	%	DIN 16901
Water absorption rate
23℃，24hr	< 0.10	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	14500	MPa	ISO 527-2
tensile strength	176	MPa	ISO 527-2
Tensile strain
yield	2.8	%	ISO 527-2
Bending modulus	12500	MPa	ISO 178
bending strength	260	MPa	ISO 178
Bending strain	3.0	%	ISO 178

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	7.0	kJ/m²
23℃	7.0	kJ/m²
Charpy Unnotch Impact strength
-30℃	45	kJ/m²
23℃	48	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	280	℃	ISO 75-2/A
Continuous use temperature	250	℃	UL 746B
Maximum operating temperature
short-term	280	℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	< 1.0E+9	ohms	IEC 60093
insulation resistance	< 1.0E+9	ohms	IEC 60167

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	V-0		UL 94

Process Conditions
Squeeze description	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method

Drying temperature	150	°C
Drying time	3.0 to 6.0	hr
Barrel 1 zone temperature	360 to 370	°C
Barrel 2 zone temperature	380 to 390	°C
Barrel 3 zone temperature	390 to 400	°C
Melt temperature	390	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.