| Ryton® XE3500BL unfilled polyphenylene sulfide alloy compound for extrusion and blow molding provides excellent mechanical strength, ductility, toughness and chemical resistance. |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Ductility,Solvent resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 316℃，5.0kg | 1.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 | % | ASTM D570 |
| Shrinkage rate | 2.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1500 | MPa | ISO 527 |
| tensile strength | 40.0 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 80 | % | ISO 527 |
| Bending modulus | 1500 | MPa | ISO 178 |
| bending strength | 60.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 50 | kJ/m² | ISO 180/A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM E1530 |
| Hot deformation temperature | |||
| 0.45 MPa | 110 | ℃ | |
| 1.8 MPa | 90 | ℃ | |
| Linear coefficient of thermal expansion | |||
| -50~50℃ | 8.0E-5 | 1/℃ | |
| 100~200℃ | 1.5E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 24 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 25 ℃，1 kHz | 3.10 | ||
| 25 ℃，1 MHz | 3.10 | ||
| Dissipation factor | |||
| 25℃，1 kHz | 2.0E-3 | ||
| 25℃，1 MHz | 5.0E-3 | ||
| Arc resistance | 120 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-1 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |