| LUVOCOM® 70-9113/BK is a Polyketone (PK) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 70-9113/BK are: Chemical Resistant Lubricated Mold Release Agent Wear Resistant Typical application of LUVOCOM® 70-9113/BK: Engineering/Industrial Parts&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | POK |
| Material Status | Commercial: Active |
| Features | Good liquidity,Low coefficient of friction,Lubricating,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 30.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.6 to 2.2 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 57.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 18 | % | ISO 527-2 |
| Bending modulus | 1500 | MPa | ISO 178 |
| bending strength | 68.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 82 | kJ/m² | ISO 179/1fU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Continuous use temperature | 90.0 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 120 | ℃ | |
| Vicat Softening Temp | 200 | ℃ | ISO 306/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+12 | ohms | IEC 60093 |
| insulation resistance | > 1.0E+12 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Hot air dryer | 120 | °C | |
| Hot air dryer, B | 80 | °C | |
| Drying time | |||
| Hot air dryer | 1.0 to 4.0 | hr | |
| Hot air dryer, B | 2.0 to 6.0 | hr | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 245 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |