Hyundai EP Adhesives LE200T/1002

About
LE200T is a polyethylene based adhesive polymer containing anhydride functionality. It is available in pellet form and designed for use in 3-layer pipe coating systems in conjunction with an epoxy primer and a thick polyethylene top-coat. LE200T has high physical properties originated from LLDPE and shows excellent processability during 3-layer pipe coating operation. Together with Yuclair ET509B (Black compounded top coat) and commercially available epoxy primer, LE200T shows highly adjusted pipe coating system available for all pipe coating specification including DIN30670, CSA Z425.21-02, NFA 49-710.&&

About

LE200T is a polyethylene based adhesive polymer containing anhydride functionality. It is available in pellet form and designed for use in 3-layer pipe coating systems in conjunction with an epoxy primer and a thick polyethylene top-coat. LE200T has high physical properties originated from LLDPE and shows excellent processability during 3-layer pipe coating operation. Together with Yuclair ET509B (Black compounded top coat) and commercially available epoxy primer, LE200T shows highly adjusted pipe coating system available for all pipe coating specification including DIN30670, CSA Z425.21-02, NFA 49-710.&&

Product Description
Supplier	HYUNDAI EP
Generic	PE
Material Status	Commercial: Active
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.927	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ASTM D1238
Water absorption rate
24hr	< 0.010	%	ASTM D570

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	100	℃	ASTM D1525

Supplementary information	Nominal value	Unit	Test method
Adhesive strength	> 3.4	kN/m	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	47		ASTM D2240
tensile strength
fracture	17.7	MPa	ASTM D638
Tensile strain
fracture	800	%	ASTM D638

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.