| About |
|---|
| 12% carbon fiber reinforced Polyetherimide (Tg 217C). ECO Conforming. UL94 V0 listing in recognized colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | ECO,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 7.5 | g/10min | ASTM D1238 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.12 to 0.22 | % | |
| TD：3.2 mm | 0.30 to 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8140 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 131 | MPa | |
| fracture | 131 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 5.1 | % | |
| fracture | 5.1 | % | |
| Bending modulus | ASTM D790 | ||
| 100 mm span | 8270 | MPa | |
| 50 mm span | 7830 | MPa | |
| bending strength | ASTM D790 | ||
| Fracture, 50 mm span | 221 | MPa | |
| Fracture, 100 mm span | 193 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 420 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 6.21 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 213 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 209 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 210 | ℃ | |
| Vicat Softening Temp | 214 | ℃ | ASTM D1525 8 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 1.4E-5 | 1/℃ | |
| MD：-20~150℃ | 1.4E-5 | 1/℃ | |
| TD：-40~40℃ | 3.2E-5 | 1/℃ | |
| TD：-20：150℃ | 4.0E-5 | 1/℃ | |
| Relative temperature index | 105 | ℃ | UL 746 |
| Electrical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 | |
| Electrostatic attenuation | 10 | msec | FTMS 101B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.57 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. 0.051 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |