| Greene, Tweed offers precision plastic components for a variety of demanding semiconductor applications. These components are made from a full range of high-performance plastic materials including Arlon® 1260, which is ideal for applications requiring high impact, wear and chemical resistance.&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ASTM D792 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 316 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| < 149℃ | 9.0E-6 | cm/cm/℃ | ASTM D696 |
| > 149℃ | 1.8E-5 | cm/cm/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 92 | ASTM D2240 | |
| Rockwell hardness | |||
| M-level | 108 | ASTM D785 | |
| Tensile modulus | |||
| 0.5% 割线 | 21700 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 230 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.9 | % | ASTM D638 |
| Bending modulus | |||
| 0.5% secant | 19000 | MPa | ASTM D790 |
| bending strength | 347 | MPa | ASTM D790 |
| compressive strength | 262 | MPa | ASTM D695 |
| shear strength | ASTM D732 | ||
| 23℃ | 120 | MPa | ASTM D732 |
| 23℃ | 95.8 | MPa | ASTM D732 |
| friction coefficient | |||
| With oneself – dynamic | 0.18 | ASTM D1894 | |
| Load deformation | 0.0600 | % | ASTM D621 |
| Wear factor | 460 | 10^-8 mm³/N·m | ASTM D3702 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. at Break |
| 3. Transverse |
| 4. Axial |
| 5. PV = 12600 psi-ft/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |