| Characteristics: Control reologhy Impact Block Copolymer polypropylene; high impact/stiffness balance; tough weld line. Recommended for: Injection molding of seats, furniture and industrial applications; compounding; housewares; injection molding general purpose applications.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Controllable rheological,Food contact compliance,Block Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 13 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 22.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 3.20 mm, injection molding | 7.5 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, 3.20 mm, injection molded | 1030 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 160 | J/m | ASTM D256-A |
| Drop hammer impact | |||
| -30 ℃, 3.2 mm, injection molding | 27.1 | J | ASTM D5420 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure B |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.051 in/min |
| 5. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |