TECHNYL® A 60X1 V30 BLACK

About
TECHNYL® A 60X1 V30 Black is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL94 V0,UL94 5VA, f1, GWIT) combined with excellent processing, mechanical and electrical performance. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production.&&

About

TECHNYL® A 60X1 V30 Black is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL94 V0,UL94 5VA, f1, GWIT) combined with excellent processing, mechanical and electrical performance. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production.&&

Product Description
Supplier	DOMO
Generic	PA66
Material Status	Commercial: Active
Features	Halogen free
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.43	g/cm³
Shrinkage rate
TD	0.80	%
MD	0.30	%
Water absorption rate
23℃，24hr	0.73	%
Outdoor applicability	f1

MECHANICAL	Nominal value	Unit
tensile strength
Fracture, 23 ℃	140	MPa
Tensile strain
Fracture, 23 ℃	3.0	%
Bending modulus
23℃	8200	MPa
bending strength
23℃	210	MPa

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	10	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	240	℃
Melting temperature	262	℃

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index
Solution A	600	V

FLAME CHARACTERISTICS	Nominal value	Unit
Flame retardant level
0.80 mm	V-0
1.60 mm	V-0
3.20 mm	V-0
Glowing wire flammability index
0.80 mm	960	℃
1.6 mm	960	℃
3.2 mm	960	℃
Igniting temperature of the hot wire
1.6 mm	775	℃
3.2 mm	775	℃

Process Conditions
Injection	Nominal value	Unit	Test method
Injection instructions	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	265 to 275	°C
Temperature in the middle of the barrel	265 to 275	°C
Front temperature of material barrel	270 to 280	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.