| COMTREX FLEXIBLE PVC 63XCF is a Cadmium Free compound typically used in interior applications such as molding decorative covers for arm rest assemblies that require wear resistance. This compound is available in custom matched black and integral colors. Gloss level will depend on mold design and application. Designed to meet Daimler Chrysler Corporation Material Standard MS-DC526.&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good wear resistance,Low to no calcium content |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 12.8 | MPa | ASTM D412A |
| tear strength | 38.7 | kN/m | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature bending | |||
| -29℃，2.50 cm | Flexible, No Cracks | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FMVSS flame retardant rating | Self-Extinguishing (SE | FMVSS 302 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Accelerated aging time | No objectionable change in color or gloss. No objectionable defects. | SAE J1885 | |
| Fog Test | Very Slight Fog | Internal Method | |
| Cold/Hot Cycle -24 hours | Internal Method | ||
| -29℃ | No splitting, cracking, loss of appearance qualities, or physical properties | Internal Method | |
| 79℃ | No splitting, cracking, loss of appearance qualities, or physical properties | Internal Method | |
| Volatile loss | |||
| 72 hours，79℃ | 0.50 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | 64 | ASTM D2240 | |
| Tensile strain | |||
| fracture | 350 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Method A, Die “C” |
| 4. Die C, 20 in/min |
| 5. 2.0 in/min |
| 6. 600 kJ/m² exposure to Interior Xenon Arc Weather-ometer per SAE J1885. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |