| About |
|---|
| Bormed TD109CF is a propylene alpha olefin copolymer. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown films on tubular water quenching process. CAS-No.: 25895-47-0 Applications Bormed TD109CF has been evaluated according to different regulations and norms. Typical applications are mentioned below for Medical devices or Pharmaceutical & Diagnostic packaging. However, Borealis should be consulted for final approval to evaluate the use of Bormed TD109CF . Medical device packaging Pouches for IV solutions This grade may only be used for the applications listed in the Product Datasheet and only to the extent that the application is within the scope of the tests set out in the Statement on Compliance to Regulations on Medical Use for that grade. If an application is not listed in the Product Datasheet, the grade can be used for such application only after express written consent of the Borealis Marketing Manager, Healthcare. Borealis prohibits the use of any healthcare grade product in an implantable device that is introduced into the human body by surgical intervention and that is intended to remain in place following surgical procedure. Special features Excellent optical properties Wide sealing window Low sealing initiation temperature Sterilisability by means of water steam High seal strength and hot tack force&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Steam sterilized,Optical performance,Thermal viscous strength,Poor moisture permeability,Broad Seal Range,Copolymer,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23 ℃, injection molding | 700 | MPa | ISO 178 |
| friction coefficient | |||
| With oneself – dynamic | > 0.70 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD，50 µm | 470 | MPa | ISO 527-3 |
| TD，50 µm | 490 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD，50 µm | 30.0 | MPa | ISO 527-3 |
| TD，50 µm | 20.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m | 450 | % | ISO 527-3 |
| TD, fracture, 50 µ m | 470 | % | ISO 527-3 |
| Dart impact equipped with measuring instruments | |||
| 50 µm，Total Energy | 12.0 | J | ISO 7765-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 130 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50 µm | > 130 | ASTM D2457 | |
| Haze | |||
| 50 µm | < 0.50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cast Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |