| Riblene FC 39 F is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 39 F is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 39 F are easily heat shrinkable and characterised by high rigidity, good mechanical and optical properties. Main Application Riblene FC 39 F is recommended for the production of medium rigidity shrink film characterized by good clarity and gloss.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,Optical performance,Food contact compliance,High molecular weight,Good melt strength,Low density,Good thermal contraction |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.25 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 70 | µm | |
| film thickness | 40-150 µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 70 µ m, blow molded film | 180 | MPa | ISO 527-3 |
| 1% secant, TD, 70 µ m, blow molded film | 190 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 70 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| TD, yield, 70 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| MD, fracture, 70 µ m, blow molded film | 28.0 | MPa | ISO 527-3 |
| TD, fracture, 70 µ m, blow molded film | 26.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 70 µ m, blow molded film | 450 | % | ISO 527-3 |
| TD, fracture, 70 µ m, blow molded film | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 70 µ m, blow molded film | 310 | g | ISO 7765-1 |
| tear strength | ISO 6383-2 | ||
| MD，70 µm | 30.0 | kN/m | ISO 6383-2 |
| TD，70 µm | 45.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 93.0 | ℃ | ISO 306/A |
| Melting temperature | 114 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 70 µ m, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| 70.0 µ m, blow molded film | 8.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |