| DEG387-8651 is a 30% glass fibre reinforced polypropylene compound with very high impact property, soft touch, UV stabilization, intended for injection moulding. DEG387-8651 has been developed especially for demanding applications in automotive industry and various engineering sectors. APPLICATIONS Electrical parts Business equipment Automotive parts&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Renewable resources,Soft,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2080 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 31.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 14 | % | ISO 527-2 |
| Bending modulus | 1840 | MPa | ISO 178 |
| bending strength | 44.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 37 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 76 | kJ/m² | ISO 179/1eU |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 210 to 260 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Injection speed | Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |