TECHNYL® A 50H1

About
TECHNYL® A 50H1 Black is an unreinforced polyamide 66 based on a non-phosphorous and non-halogenated flame retardant system, heat stabilized, for injection moulding. This flame retardant grade, offers excellent filling qualities combined with good stiffness.&&

Product Description
Supplier	DOMO
Generic	PA66
Material Status	Commercial: Negative
Features	Good stripping performance,Low to no phosphorus content,Halogen free
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.16	g/cm³	ISO 1183
Water absorption rate	0.88	%	ISO 62
23°C，24 hr
Mold shrinkage rate
Parallel: 23 ° C, 50% RH, 72 hr	1.3	%	ISO 294-4,2577
Normal: 23 ° C, 50% RH, 72 hr	0.95	%	ISO 294-4,2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min	3800	MPa	ISO 527-1/-2
Tensile stress
fracture	75	MPa	ISO 527-1/-2
Tensile strain
fracture	9	%	ISO 527-1/-2
Bending modulus
2 mm/min	3700	MPa	ISO 178
2 mm/min	3800	MPa	ASTM D790
bending strength
2 mm/min	130	MPa	ISO 178
2 mm/min	120	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23°C	80	kJ/m²	ISO 179/1eU
-30°C	80	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23°C	3.2	kJ/m²	ISO 180/1A
-30°C	3	kJ/m²	ISO 180/1A
Impact strength of cantilever beam notch
23°C	3	KJ/m²	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Melting temperature	263	℃	ISO 11357-1
Hot deformation temperature
0.45 MPa	237	℃	ISO 75
1.80 MPa	85	℃	ISO 75

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	3E+13	ohms·cm	IEC 62631-3-1
Surface resistivity	3E+15	ohm	IEC 62631-3-1
Compared to the leakage tracing index
Solution A	600	V	IEC 60112
Dielectric strength
1 mm	21	kV/mm	IEC 60243-1

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
0.40 mm	V-0		UL 94
0.75 mm	V-0		UL 94
1.5 mm	V-0		UL 94
3.0 mm	V-0		UL 94
Glowing wire flammability index
0.75 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire
0.40 mm	960	℃	IEC 60695-2-13
0.75 mm	960	℃	IEC 60695-2-13
1.5 mm	775	℃	IEC 60695-2-13
Oxygen index	33	%

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.2	%
Temperature at the rear of the barrel	260 – 270	°C
Temperature in the middle of the barrel	265 – 275	°C
Front temperature of material barrel	265 – 275	°C
Mold temperature	60 – 80	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.