| HDPE GM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process. Applications: Bags in general (such as T-shirt bags, hancle bags, star bags, others); geomembranes. Process: Blown Film Extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Wide molecular weight distribution,Food contact compliance,High molecular weight,High density |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，21.6kg | 9.3 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 0.33 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, TD, 13 µ m, blow molded film | 870 | MPa | ASTM D882 |
| 1% secant, MD, 13 µ m, blow molded film | 750 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 13 µ m, blow molded film | 45.0 | MPa | ASTM D882 |
| TD, yield, 13 µ m, blow molded film | 30.0 | MPa | ASTM D882 |
| MD, fracture, 13 µ m, blow molded film | 85.0 | MPa | ASTM D882 |
| MD, yield, 13 µ m, blow molded film | 40.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 13 µ m, blow molded film | 740 | % | ASTM D882 |
| TD, yield, 13 µ m, blow molded film | 5.0 | % | ASTM D882 |
| MD, fracture, 13 µ m, blow molded film | 590 | % | ASTM D882 |
| MD, yield, 13 µ m, blow molded film | 15 | % | ASTM D882 |
| Drop hammer impact | |||
| 13 µ m, blow molded film | 200 | g | ASTM D1709 |
| tear strength | |||
| TD, 13 µ m, blow molded film | 50 | g | ASTM D1922 |
| MD, 13 µ m, blow molded film | 5.0 | g | ASTM D1922 |
| Sealing starting temperature | |||
| 13 µ m, blow molded film | 125 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |