| About |
|---|
| PETLIN LD N125Y is a low density polyethylene resin for general purpose film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free), slip and antiblock additives. It is intended primarily for blown film process.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Smoothness,High anti-blocking,Low speed solidification point,Food contact compliance,Inoxidizability |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.10 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 20 to 100 µm | ||
| Tensile modulus | ISO 527-3 | ||
| MD，25 µm | 194 | MPa | |
| TD，25 µm | 216 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m | 70.0 | MPa | |
| TD, fracture, 25 µ m | 25.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m | 130 | % | |
| TD, fracture, 25 µ m | 580 | % | |
| Drop hammer impact | |||
| 25 µm | 77 | g | ASTM D1709 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：25 µm | 70000 | N | |
| TD：25 µm | 25000 | N |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，25 µm | 61 | ASTM D2457 | |
| Haze | |||
| 25 µm | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |