| About |
|---|
| ETILINAS PC4020 is designed specifically for coating/cladding of metal pipes and tubes. ETILINAS PC4020 is based on a special medium dencity copolymer with exceptionally high resistance to environmental stress cracking and contains suitable additives necessary for ease of coating manufacture and to ensure long term weathering resistance.&& |
| Product Description | |
|---|---|
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Copolymer,High ESCR |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.947 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F0 | 1000 | hr | ASTM D1693B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -100 | ℃ | ASTM D746 |
| Vicat Softening Temp | 116 | ℃ | ISO 306/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 25 | kV/mm | ASTM D149 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second | 60 | ISO 868 | |
| tensile strength | |||
| yield | 19.0 | MPa | ISO 527-2/2 |
| Tensile strain | |||
| fracture | 600 | % | ISO 527-2/2 |
| Bending modulus | 750 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 225 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |