| 532L is a low-density polyethylene resin for skin layer of multi-layer lamination films. This grade is designed to be processed in conventional blown film equipment.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,Good heat sealing,Optical performance,Low speed solidification point,Good Tensile Strength,Low density |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.8 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23℃ | 275 | MPa | ASTM D747 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ASTM D882 | ||
| fracture | 12.7 | MPa | ASTM D638 |
| MD, yield, 40 µ m | 22.6 | MPa | |
| TD, yield, 40 µ m | 15.7 | MPa | |
| Tensile strain | ASTM D882 | ||
| fracture | 700 | % | ASTM D638 |
| MD, fracture, 40 µ m | 240 | % | |
| TD, fracture, 40 µ m | 590 | % | |
| Drop hammer impact | |||
| 40 µm | 65 | g | ASTM D1709 |
| Initial sealing temperature | |||
| 40 µm | 140 | ℃ |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 95.0 | ℃ | ASTM D1525 1 |
| Melting temperature | 113 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，40 µm | 75 | ASTM D2457 | |
| Haze | |||
| 40 µm | 6.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 130 to 150 | °C | |
| Barrel 2 zone temperature | 130 to 150 | °C | |
| Barrel 3 zone temperature | 130 to 150 | °C | |
| Barrel 4 zone temperature | 130 to 150 | °C | |
| Barrel 5 zone temperature | 130 to 150 | °C | |
| Melt temperature | 160 | °C | |
| Nozzle temperature | 160 to 170 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |