AMPLIFY™ TY 1053H

About
AMPLIFY™ TY 1053H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene. In tie layers for flexible packaging, AMPLIFY TY 1053H Functional Polymer promotes adhesion of polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Typical blending levels in polyethylene let-down resin are 12-20% for EVOH and 6-12% for nylon. Main Characteristics: Maleic anhydride modified HDPE Adhesive concentrate for use in blown, cast, and coating applications Tie layer for food packaging and pipe coating Adhesive layer in multi-layer flexible film applications Polymer compatibilizer Complies with: U.S. FDA 21 CFR 177.1520(c)6 EU, No 10/2011 Consult the regulations for complete details.&&

About

AMPLIFY™ TY 1053H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene. In tie layers for flexible packaging, AMPLIFY TY 1053H Functional Polymer promotes adhesion of polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Typical blending levels in polyethylene let-down resin are 12-20% for EVOH and 6-12% for nylon. Main Characteristics: Maleic anhydride modified HDPE Adhesive concentrate for use in blown, cast, and coating applications Tie layer for food packaging and pipe coating Adhesive layer in multi-layer flexible film applications Polymer compatibilizer Complies with: U.S. FDA 21 CFR 177.1520(c)6 EU, No 10/2011 Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	马来酸酐接枝共聚物
Material Status	Commercial: Active
Availabilitys	North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.958	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	2.0	g/10min	ASTM D1238，ISO 1133
MAH grafting level	Very High		Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	129	℃	ASTM D1525 , ISO 306
Melting temperature
DSC	130	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ASTM D2240 , ISO 868
Shaw’s A	98		ASTM D2240 , ISO 868
Shaw’s D	67		ASTM D2240 , ISO 868
tensile strength
fracture	15.9	MPa	ASTM D638
fracture	15.9	MPa	ISO 527-2/51
Tensile strain
fracture	300	%	ASTM D638
fracture	300	%	ISO 527-2/51
Bending modulus
2% secant	924	MPa	ASTM D790A , ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
2. Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt%, Very High >1.0 wt%.
3. 2.0 in/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.