Nycast SLX - SOLIAO

About
NYCAST SLX joins the NYCAST family of premium bearing grades as an engineering and design solution for bearing and wear applications. NYCAST SLX closes the gap between static and dynamic coefficients of friction with superior performance where customers require the best material for overcoming “stick-slip” tendencies. Unlike the competition, Cast Nylons Limited offers SLX in all our standard stock shape configurations. We never limit your design to only a few options. This is one more reason to put the NYCAST Advantage to work for you. Manufactured with a proprietary lubrication package, NYCAST SLX is available as plate up to 4″ thick, rod up to 12″ diameter, and tubular bar up to 40″ diameter.&&

About

NYCAST SLX joins the NYCAST family of premium bearing grades as an engineering and design solution for bearing and wear applications. NYCAST SLX closes the gap between static and dynamic coefficients of friction with superior performance where customers require the best material for overcoming “stick-slip” tendencies. Unlike the competition, Cast Nylons Limited offers SLX in all our standard stock shape configurations. We never limit your design to only a few options. This is one more reason to put the NYCAST Advantage to work for you. Manufactured with a proprietary lubrication package, NYCAST SLX is available as plate up to 4″ thick, rod up to 12″ diameter, and tubular bar up to 40″ diameter.&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Good wear resistance
Availabilitys	North America
Process Methods	casting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.12 to 1.14	g/cm³	ASTM D792
Water absorption rate
24hr	0.032	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	74 to 80	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	216	℃	ASTM D648
1.8 MPa, unannealed	70.0 to 72.2	℃	ASTM D648
Melting temperature	221	℃
Linear coefficient of thermal expansion
MD	7.5E-5	1/℃	ASTM D696

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	75 to 84		ASTM D2240
Rockwell hardness
R-level	113 to 120		ASTM D785
Tensile modulus	3170	MPa	ASTM D638
tensile strength	69.6 to 70.3	MPa	ASTM D638
Tensile strain
fracture	38 to 47	%	ASTM D638
Bending modulus	2510 to 2590	MPa	ASTM D790
bending strength	86.9 to 89.6	MPa	ASTM D790
Compression modulus	1870 to 1970	MPa	ASTM D695
compressive strength	101 to 112	MPa	ASTM D695
shear strength	58.9 to 59.2	MPa	ASTM D732
friction coefficient			ASTM D1894
With oneself – dynamic	0.14 to 0.19		ASTM D1894
With oneself – static	0.12 to 0.14		ASTM D1894
Load deformation	0.510	%	ASTM D621

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.