| About |
|---|
| 3M™ Dyneon™ FPO 3730 is a peroxide curable fluoroelastomer terpolymer containing 69.8 wt% fluorine. FPO 3730 can be used in compression, transfer or injection molding, and extrusion processes. Features and Benefits Good processability Excellent physicals Broad chemical resistance&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity,Solvent resistance,Terpolymer,Fuel resistance |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.89 | g/cm³ | Internal Method |
| Mooney viscosity | |||
| ML 1+10，121℃ | 35 | MU | Internal Method |
| Fluorine content | 70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 74 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 23.8 | MPa | DIN 53504 |
| 100% strain | 8.40 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 180 | % | DIN 53504 |
| Compression deformation | |||
| 150℃，22 hr | 62 | % | ASTM D395 |
| 200℃，70 hr | 30 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -9.00 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Post Cure 16 Hours @ 232°C (450°F) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |