| About |
|---|
| InnoPlus HD2401C is high density polyethylene which is highly recommended for injection molding and compression molding process. This grade provides easy processing characteristic with high stiffness, good tensile strength and exhibits excellent organoleptic properties. Typical Application : Beverage caps for drinking and mineral water.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Food contact compliance,Good sensory characteristics.,Good Tensile Strength,High density |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, F50 | 2.00 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 29 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression molding temperature | 140 to 165 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ASTM D2240 | |
| tensile strength | |||
| yield | 30.4 | MPa | |
| fracture | 11.8 | MPa | |
| Tensile strain | |||
| fracture | 750 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1080 | MPa | ASTM D747 |
| Bending modulus | 1570 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Complete Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |