| About |
|---|
| CELEX 5200HF.IM advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. Its superior processing makes it ideal for molding large parts and optimizing cycle time productivity in injection molding operations. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics markets. Main Characteristics: UL 94 V-0 @ 1.5mm Applications: TV, monitor and PC enclosures Adaptors and chargers&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 230℃，3.80kg | 17 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 75 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 62.1 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 46.2 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 4.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 50 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2830 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 97.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm, injection molded | 93.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 82.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 108 | ℃ | ASTM D1525 4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Extreme oxygen index | 29 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 to 91 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 60 to 91 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |