| About |
|---|
| PERLEX® R3510 is a Polycarbonate (PC) material filled with 10% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of PERLEX® R3510 are: Flame Rated Flame Retardant Typical application of PERLEX® R3510: Engineering/Industrial Parts&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4050 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 75.0 | MPa | ISO 527-2 |
| Bending modulus | 3900 | MPa | ISO 178 |
| bending strength | 135 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，Area | 10.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 128 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 135 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 960 | ℃ | IEC 60695-2-13 |
| 2 mm | 960 | ℃ | IEC 60695-2-13 |
| 3 mm | 960 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |