BMC 5307 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a medium impact material produced in extruded form for ease of handling. Other characteristics are good overall electrical properties and flame resistance. Typical applications include circuit breakers, transformer bobbins and motor end bells. BMC 5307 molding compound is produced in extruded form in a range on industrial colors. It is available in logs 12 inches in length and from 1″ to 2 ½” in diameter Within this range, smalle r diameters are supplied as multiple extrusions and weight tolerances are plus or minus5%, up to a maximum of plus or minus 15 grams.&&

About

BMC 5307 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a medium impact material produced in extruded form for ease of handling. Other characteristics are good overall electrical properties and flame resistance. Typical applications include circuit breakers, transformer bobbins and motor end bells. BMC 5307 molding compound is produced in extruded form in a range on industrial colors. It is available in logs 12 inches in length and from 1″ to 2 ½” in diameter Within this range, smalle r diameters are supplied as multiple extrusions and weight tolerances are plus or minus5%, up to a maximum of plus or minus 15 grams.&&

Product Description
Generic	热固性聚酯
Material Status	Commercial: Active
Features	Good Electrical Properties,Flame Characteristics
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.01	g/cm³
Water absorption rate	0.10	%
Shrinkage rate	0.22 – 0.40	%

Electrical performance	Nominal value	Unit	Test method
Insulation strength	13.8	KV/mm
Arc resistance	>= 185	sec

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
	1.59 mm	V-0	UL 94
	3.17 mm	V-0	UL 94
	6.35 mm	V-0	UL 94

Other performance	Nominal value	Unit	Test method
Compared to the leakage tracing index	>= 600	V

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	214 – 267	J/m

MECHANICAL	Nominal value	Unit
	30 – 45
tensile strength	55.2 – 68.9	MPa
bending strength	110 – 138	MPa
compressive strength	152 – 179	MPa

Process Conditions
injection	Nominal value	Unit	Test method
Injection temperature
Mold temperature	138-177	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. Method A (Short-Time)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.