| SEALUTION™ 230 Peel Polymer is a high clarity peelable sealant that gives a peelable seal to itself, polypropylene and polyethylene. It is suitable for use in cast film lines. Main Characteristics: Pellet form Peelable sealant to itself, PP and PE Good optics Complies with: EU, No 10/2011 U.S. FDA Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.897 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.3 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Initial sealing temperature | |||
| 51 µ m, blow molded film | 95.0 | ℃ | Internal Method |
| Strippable range | 95 to 180 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 50 µ m, blow molded film | < 10 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Temperatures at which 2 N/15 mm heat seal strength is achieved. Heat Seal Strengths, Topwave HT Tester 0.5 s dwell, 500 N pressure, pull speed 100 mm/min. |
| 3. Peelable range of 3-5 N/15 mm. for this particular structure, seal to itself. Heat Seal Strengths, Topwave HT Tester 0.5 s dwell time, 500 N pressure, pull speed 100 mm/min. |
| 4. Haze for this particular structure |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |