| 20% glass fibre reinforced flame-retardant Polyamide 6 grade (V-2); halogen free&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4600 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 60.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 7.0 | % | ISO 527-2/1A/5 |
| Bending modulus | 4000 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| 9% strain | 95.0 | MPa | ISO 178 |
| 3.50% strain | 100 | MPa | ISO 178 |
| 6% strain | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 140 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 205 | ℃ | ISO 75-2/Bf |
| Continuous use temperature | 90.0 | ℃ | |
| Vicat Softening Temp | |||
| A50 | 215 | ℃ | ISO 306/A50 |
| B50 | 205 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 35 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.8 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.6 mm | V-2 | IEC 60695-11-10, -20 | |
| 3.2 mm | V-2 | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.75 mm | 725 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 725 | ℃ | IEC 60695-2-13 |
| 3 mm | 725 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Proposed maximum recycled material ratio | 25 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection pressure | 80.0 to 140 | MPa | |
| Injection speed | Slow-Moderate | ||
| Hold pressure | 40.0 to 85.0 | MPa | |
| Back pressure | 2.00 to 8.00 | MPa | |
| Screw speed | < 250 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Long periode (20000h) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |