| About |
|---|
| SARANEX 750 is a multilayer barrier film designed for ostomy and similar pouching applications. It is designed with soft haptics and is high frequency (HF or RF) sealable. It is also heat sealable. It has excellent barrier to oxygen, and aromas. General Characteristics: Available Colors: clear, beige Gauge Range: 3.0 mil (76 µm) Width Range: 5-80 inches (127-2032 mm)&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | PVDC |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | 0.30 | Internal Method | |
| Ultimate Tensile Strength | ASTM D882 | ||
| MD | 20.7 | MPa | ASTM D882 |
| TD | 17.2 | MPa | ASTM D882 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen transfer rate | 8.5 | cm³/m²/24 hr | Internal Method |
| Heat sealing strength | Internal Method | ||
| MD | 610 | N/m | Internal Method |
| TD | 610 | N/m | Internal Method |
| dosage | |||
| clear film，76.2 µm | 0.0133 | m²/kg | ASTM D4321 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface energy | |||
| fresh | 48.0 | dynes/cm² | ASTM D2578 |
| Tensile strain | |||
| MD, fracture | 350 | % | ASTM D882 |
| TD | 400 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. kinetic, in-to-out |
| 3. 350°F (177°C), 1 sec preheat, 1 sec dwell time, 30 psi (2.1 Bar) pressure. |
| 4. 350°F (177°C), 1 sec preheat, 1 sec dwell time, 30 psi (2.1 Bar) pressure |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |