| About |
|---|
| FA6220 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Includes Antioxidant. This grade is developed for the production of thin blown films. CAS-No.: 9002-88-4 Applications FA6220 has been developed especially for applications like: Shrink film General packaging film Pouches Bubble film and foam Additives FA6220 contains antioxidant.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Inoxidizability,High pressure heat resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.1 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| With oneself – dynamic | 0.90 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| Membrane puncture energy | |||
| 40 µm | 1.30 | J | ASTM D5748 |
| Secant modulus | |||
| TD，40 µm | 210 | MPa | ASTM D882A |
| MD，40 µm | 200 | MPa | ASTM D882A |
| tensile strength | ISO 527-3 | ||
| MD，40 µm | 26.0 | MPa | ISO 527-3 |
| TD，40 µm | 20.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 41 µ m | 350 | % | ISO 527-3 |
| TD, fracture, 41 µ m | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µm | 100 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：40 µm | 5.0 | N | ISO 6383-2 |
| TD：40 µm | 3.0 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 111 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 40 µm | 85 | ASTM D2457 | |
| Haze | |||
| 40 µm | 7.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown FIlm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |