| About |
|---|
| Nypel RC6030F BK is a heat stabilized, 30% glass fiber reinforced, black injection molding grade produced with at least 20% recycled PA6 feedstock. This product is a regional grade available in North America only. Applications Nypel RC6030F BK is generally recommended for applications such as bolts, racks, automotive underhood components, pressure regulator housings and caps.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.7 | % | ISO 62 |
| saturated | 6.7 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | ISO 62 |
| Balance, 50% RH | 1.9 | % | ASTM D570 |
| 24hr | 1.1 | % | ASTM D570 |
| 23℃，24hr | 1.1 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 8.0 | kJ/m² | ISO 179 |
| 23℃ | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 205 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 203 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 218 | ℃ | ISO 75-2/B |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD | 6.7E-5 | 1/℃ | |
| MD | 3.8E-5 | 1/℃ | ASTM E831 |
| MD | 2.5E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9500 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 165 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 155 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8700 | MPa | ISO 178 |
| 23℃ | 8480 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 230 | MPa | ISO 178 |
| 23℃ | 235 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 83 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |