| Moplen EP200R Moplen EP200R is the reactor TPO manufactured by PMC under the license of BASELL using the Spheripol process. Moplen EP200R is a super impact copolymer particularly suitable for injection molding of high impact resistance required application and compounding base resin of automotive bumper fascia and containers.&&Moplen EP200R Moplen EP200R is a “Reactor-made Thermoplastic PolyOlefin”, super impact copolymer with high impact resistance. Typical customer application is compounding base resin for automotive bumper fascia.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | TPU |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,High impact resistance,low-temperature impact resistance,Impact copolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 21 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 130 | J/m | ASTM D256 |
| 23℃ | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 130 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 30 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 60 | ASTM D2240 | |
| Rockwell hardness | |||
| R-level | 50 | ASTM D785 | |
| tensile strength | |||
| yield | 17.7 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| Bending modulus | 735 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |