| About |
|---|
| Clyrell EC508 is a specially designed nucleated polypropylene copolymer, with low stress whitening, low shrinkage, high gloss, and good stiffness impact balance. Typical customer applications are toys, sports and leisure goods, containers, housewares, consumer goods, and base resin for compounding for parts of automotive, electrical and electronic appliances.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,Low contractility,Nucleation |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -20℃ | 40 | J/m | |
| 23℃ | 150 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 50 | ||
| tensile strength | |||
| yield | 22.0 | MPa | |
| Tensile strain | |||
| yield | 11 | % | |
| Bending modulus | 1080 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |