| About |
|---|
| PolyAxis LL 8461 is a linear low density polyethylene intended for the rotational molding industry. Offers excellent ESCR and toughness. |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Hexene copolymers,High ESCR |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.3 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, molded, F50 | 60.0 | hr | |
| 100% non-ionic detergent, molded, F50 | > 1000 | hr | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength (yield, roll forming) | 19.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, roll forming | 240 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, roll forming | 834 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| impact strength | |||
| -40 ° C, 3.18 mm, roll forming | 75 | J | |
| -40 ° C, 6.35 mm, roll formed | > 258 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 58.9 | ℃ | |
| 1.8 MPa, unannealed | 38.9 | ℃ | |
| Melting peak temperature | 126 | °C | ASTM D3418 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |