| Lotrène® Q2018C can be processed at optimal output rates with moderate extrusion pressure, good web stability and gauge control on cast film machines designed for LLDPE. Lotrène® Q2018C can advantageously be blended with LDPE or other PE resins used in cast film mono extrusion or co-extrusion to improve film properties. Lotrène® Q2018C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films.&& |
| Product Description | |
|---|---|
| Supplier | QAPCO |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture strength | |||
| 20 µm | 1.60 | J | ASTM D5748 |
| Membrane puncture force | |||
| 20 µm | 25.0 | N | ASTM D5748 |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 20 µ m, cast thin film | 165 | MPa | ASTM D882 |
| 1% secant, TD: 20 µ m, cast thin film | 170 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 20 µ m, blow molded film | 9.70 | MPa | ASTM D882 |
| TD, yield, 20 µ m, blow molded film | 9.60 | MPa | ASTM D882 |
| MD, fracture, 20 µ m, blow molded film | 37.0 | MPa | ASTM D882 |
| TD, fracture, 20 µ m, blow molded film | 23.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 20 µ m, extruded film | 330 | % | ASTM D882 |
| TD, fracture, 20 µ m, extruded film | 670 | % | ASTM D882 |
| Drop hammer impact | |||
| 20 µ m, cast thin film | 35 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 20 µ m, cast thin film | 12 | g | ASTM D1922 |
| TD: 20 µ m, cast thin film | 190 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 121 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 20 µ m, cast thin film | 92 | ASTM D2457 | |
| Haze | |||
| 20.0 µ m, cast thin film | 1.8 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Extrusion rate | > 6.7 | m/sec |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 180 to 250 | °C | |
| Barrel 2 zone temperature | 180 to 250 | °C | |
| Barrel 3 zone temperature | 180 to 250 | °C | |
| Barrel 4 zone temperature | 180 to 250 | °C | |
| Barrel 5 zone temperature | 180 to 250 | °C | |
| Melt temperature | 220 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |