| About |
|---|
| NORYL GTX NX0013 is a conductive, high heat material. It is especially designed for in- and on-line painted bodypanels and fenders in particular, with conductivity for electro-static painting in an unique way.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.3 to 1.7 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 4.2 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| -20℃ | 10 | kJ/m² | |
| 23℃ | 14 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 178 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B50 | 185 | ℃ | ISO 306 |
| B120 | 186 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 1.1E-4 | 1/℃ | |
| TD：23~80℃ | 1.1E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 to 1.0E+4 | ohms·cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 100 | MPa | ISO 2039-1 |
| Tensile modulus | 2150 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | |
| fracture | 50.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| fracture | 40 | % | |
| Bending modulus | 2200 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 320 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |