| About |
|---|
| Vi-Chem PVC VNC90-80E是一种聚氯乙烯材料,。 该产品在北美洲有供货,。 Vi-Chem PVC VNC90-80E的典型应用领域为:汽车行业&& |
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 47 | ASTM D2240 | |
| tensile strength | |||
| fracture | 20.0 | MPa | ISO 527-2/5A |
| Tensile strain | |||
| fracture | 320 | % | ISO 527-2/5A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 130 | kN/m | ISO 34-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature flexibility | |||
| -30℃ | Pass |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air (80 ℃, 1008 hr) | 7.8 | % | ASTM D573 |
| The rate of change in ultimate elongation in air | |||
| 80℃，1008 hr | 0.80 | % | ASTM D573 |
| Change in Mass in Air（80.0℃，1010 hr） | 2.7 | % | ASTM D573 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Arizona Weathering（Delta E） | 0.680 | ||
| Color stability | |||
| Delta E，80℃ | 0.360 | ASTM D573 | |
| Florida Weathering（Delta E） | 0.430 | ||
| Hydrogen Sulfide Staining | 5 AATCC | ||
| Paint Staining | No Stain |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |