| LOTRYL® BESTPEEL 2407 is a ready-to-use thermoplastic composition designed to make peelable heat seal layers onto various substrates. The base resin is a random copolymer of ethylene and methyl acrylate, polymerized by high-pressure process in autoclave reactor. Modification is introduced to ensure the best processability in the different film technologies, and the suitable properties in heat sealing and peeling. Applications LOTRYL® BESTPEEL 2407 is used as top layer of laminates in order to provide the functions of heat sealability onto various substrates like PP, PS, PET and PVC, and easy opening by interfacial peeling. LOTRYL® BESTPEEL 2407 is easily processed using the technologies of coextrusion coating, cast film coextrusion, blown film coextrusion or sheet coextrusion, to produce multilayers that can be used as lids, either directly or after lamination with other films.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EMA |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good heat sealing,Random copolymer,High pressure heat resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 to 8.0 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 6.0 to 8.0 | g/10min | ISO 1133 |
| Methacrylic acid content | 23.0 to 25.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw A, molded | 79 | ASTM D2240 | |
| Shaw A, molded | 79 | ISO 868 | |
| tensile strength | |||
| Fracture, molded | 6.00 | MPa | ISO 527-2 |
| fracture | 6.00 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 750 | % | ISO 527-2 |
| Fracture, molded | 750 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 10.0 | MPa | ASTM D790 |
| Compression Molding | 10.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | < 40.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | < 40.0 | ℃ | ISO 306/A |
| Melting temperature | 69.0 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |