| Type: Estane® 58206 is an 85A aromatic Polyester-Based Thermoplastic Polyurethane (TPU). Features: Good Flexibility at Low Temperatures and Improved Weathering Performance. Uses: Flat Die/Cast Film Extrusion and Hose/Profile Extrusion, Injection Molding.&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Aromatic,Low temperature toughness |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD | 1.4 | % | ASTM D955 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | |||
| 200% strain | 10 | % | ASTM D412 |
| tensile strength | ASTM D412 | ||
| Fracture, 0.762 mm | 48.3 | MPa | ASTM D412 |
| 100% strain, 0.762 mm | 5.50 | MPa | ASTM D412 |
| 300% strain, 0.762 mm | 10.4 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 0.762 mm | 550 | % | ASTM D412 |
| tear strength | |||
| 0.762 mm | 88.3 | kN/m | ASTM D624 |
| cracking | 23 | kN/m | ASTM D470 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume change | |||
| in Jet Fuel JP8 | 7.7 | % | ASTM D471 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -32.0 | ℃ | DSC |
| Melting temperature | 160 | ℃ | DSC |
| Kofler Melting Temperature | 155 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 5 seconds | 82 to 88 | ASTM D2240 | |
| Taber abraser | |||
| 1000 cycles, 1000 g, H-18 wheels | 20.0 | mg | ASTM D3389 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 104 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 177 | °C | |
| Barrel middle temperature | 188 | °C | |
| Barrel front temperature | 193 | °C | |
| Nozzle temperature | 199 | °C | |
| Processing (melt) temperature | 199 | °C | |
| Injection pressure | 21.0 to 48.0 | MPa | |
| Drying temperature | 104 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 177 | °C | |
| Barrel 2 zone temperature | 183 | °C | |
| Barrel 3 zone temperature | 188 | °C | |
| Barrel 4 zone temperature | 194 | °C | |
| Connector temperature | 194 | °C | |
| Melt temperature | 191 | °C | |
| Nozzle temperature | 194 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |