| Description Non-flammable PP FB11T1 and FB11ST1 are Widely used for extrusion Molding parts of pipe, sheet, etc., as it allows excellent extrusion moldability,high non-flammability, and fabulous exterior. Characteristics FB11T1: Being Widely used for non-flammable Corrugate tube, non-flammable pipe, etc. Provide fluidity and high shock resistance as a non-flammability grade ofUL94 V-2. Applications Automobile Corrugate tube (FB11T1) Other automobile/electric/electronic/industrial parts needing non-flammability With extrusion molding (FB11T1, FB11ST1)&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | noise reduction,Flame Characteristics,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.8 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.1 to 1.7 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 740 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 87.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.79 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 75 | ASTM D785 | |
| tensile strength | |||
| yield | 27.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 450 | % | ASTM D638 |
| Bending modulus | 1130 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Barrel 1 zone temperature | 170 to 180 | °C | |
| Barrel 3 zone temperature | 180 to 200 | °C | |
| Barrel 5 zone temperature | 180 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |