| HDPE 9260: High Barrier grade, good processability, high stiffness, low gels Applications: Cereal liners, cracker over-wrap, bakery mixes, specialty monolayer films, coextruded films&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low speed solidification point,High density,Block resin |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Secant modulus | ASTM D882A | ||
| 1% secant, MD: 51 µ m | 965 | MPa | |
| 2% secant, MD: 51 µ m | 758 | MPa | |
| 1% secant, TD: 51 µ m | 1240 | MPa | |
| 2% secant, TD: 51 µ m | 931 | MPa | |
| tensile strength | ASTM D882A | ||
| MD, yield, 51 µ m | 29.0 | MPa | |
| TD, yield, 51 µ m | 24.8 | MPa | |
| Tensile strain | ASTM D882A | ||
| MD, fracture, 51 µ m | 850 | % | |
| TD, fracture, 51 µ m | 500 | % | |
| Water vapor transmittance | |||
| 38℃，51 µm | 1.9 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 135 | ℃ | ASTM D3417 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 193 to 221 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1.0 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |